Melting process and melt structure of fly ash/magnesium slag blends for the production of inorganic fibers

Fiber production from inorganic industrial solid wastes is an effective waste management strategy. Because of cost considerations, most enterprises generally use local solid wastes as raw materials to produce fibers. In this study, we explored the feasibility of producing fibers using fly ash and magnesium slag. The results show that the melting temperature of the blends composed of fly ash, magnesium slag, and a small amount of calcined dolomite first decreased and then increased with an increase in acidity coefficient (M_k) from 1.0 to 2.4_. The samples could form a eutectic system in the M_k range of 1.4–1.8, and therefore have a relatively low melting temperature in this M_k range. Fly ash could react with magnesium slag and calcined dolomite to form akermanite, gehlenite-magnesium, and anorthite at temperatures close to the melting temperature; therefore, these crystalline phases were the main reaction products formed in the samples with M_k values lower than 1.80. Anorthite reacted further with some Na-containing and Si-containing spieces to produce labradorite. Thus, the content of anorthite and labradorite rapidly increased and they became the major crystal phases in the blend samples with M_k values greater than 1.80. MAS-NMR spectroscopic analysis revealed that the network structure of the melts depended on the ratio of bridging oxygen to non-bridging oxygen; a high ratio of bridging oxygen to non-bridging oxygen could lead to the formation of a dense network structure in the melt. The blends of fly ash and magnesium slag can be used to produce wool fibers and continuous fibers. In addition, the suitable temperature ranges for the production of both types of fibers were determined. The drawing temperature for continuous fiber production depended on the degree of polymerization and structure of the melt.     

Development of vibration damping materials based on butyl rubber: A study of the phase equilibrium,rheological, and dynamic properties of compositions

A detailed study of butyl rubber-based vibration damping formulations linking their composition, morphology, phase structure, viscosity, mechanical loss factor, and other characteristics is presented for the first time. High performance of the compositions including aromatic petroleum oil is explained by limited solubility of the plasticizer that leads to the formation of a highly-viscous emulsion (η_20°C ≈ 1000 Pa·s) consisting of a swollen butyl rubber matrix and dispersed oil droplets in the broad composition range. Chalk is found to be the best inorganic filler as its spherical particles provide strong adhesion to the reinforcing layer of aluminum foil. Aiming to eliminate ecologically unfriendly aromatic compounds, a new low-cost binding agent formulation based on butyl rubber mixed with polyisobutylene and highly refined mineral oil is suggested. Being environmentally safe, it possesses high viscosity of 1000–3000 Pa·s, cohesion strength of 3.5–5.0 N/cm, penetration of 4.5–6.0 mm, and mechanical loss factor up to 0.34 at room temperature, which are as good as, or even better than, the properties of currently produced vibration damping materials containing aromatic compounds. New materials can be used in car and aircraft parts for effective vibration isolation.     

Effect of microwave sintering on the microstructure and mechanical properties of AA7075/B4C/ZrC hybrid nano composite fabricated by powder metallurgy techniques

AA7075 + 6%B4C+3%ZrC nano hybrid composite was successfully fabricated, with nano reinforcements composition in AA7075 alloy selected based on previous investigation, to achieve better mechanical performance. Two different sintering techniques, namely conventional and microwave, were implemented to determine the effect on microstructural and mechanical properties. Microstructural investigation was performed with the help of W-SEM. Tensile, compression, and hardness were measured with the help of UTM and Vickers microhardness machine. Porosity was calculated by using Archimedes principle. It was observed that the added nano ZrC particles formed agglomerates and the B₄C particles were distributed homogenously. Composites processed by microwave sintering showed excellent mechanical properties compared to the conventionally sintered composites. No intermetallic compounds were detected in microwave sintered composites through XRD analysis, indicating strong and clean interface bonds between matrix and reinforcement particles. High strain to fracture value of 12.24% was noted in microwave sintered nano hybrid composite, while it was 6.12% for conventional sintered one. Fractography revealed no peeling action of reinforcements from the matrix material, and the mode of failure was brittle. It was concluded that, while fabricating nano range hybrid composites, the implementation of advanced sintering technique (microwave sintering) with low sintering temperatures and low sintering times with internal heat generations, helps in eliminating defects that may develop because of high surface energies of nano range reinforcements.     

Impact behavior of aminosilane functionalized nanosilica based shear thickening fluid impregnated Kevlar fabrics

In the present work, two types of shear thickening fluids have been synthesized by using neat and aminosilane functionalized silica nanoparticles and their viscosity curves have been obtained by the rheometer. Based on the values of peak viscosity of synthesized shear thickening fluids, the surface functionalized nanosilica based shear thickening fluid has been chosen as a best candidate due to the high viscosity for impregnation into the neat Kevlar of different layers viz. four (04) and eight (08) layers for velocity impact study. The experimental investigations reveal high energy absorption of shear thickening fluid impregnated Kevlar as compared to the neat Kevlar. The maximum energy absorption 62 J is achieved corresponding to the initial velocity 154 m∙s⁻¹ for 08 layers shear thickening fluid impregnated Kevlar specimen. The data have also been analytically determined and validated with the experimental data. The experimental data have good agreement with the analytical data within the accuracy of around 15 to 20%. The present findings can have significant inferences towards the fabrication of shear thickening fluids using nanomaterials for numerous applications such as soft armors, dampers, nanofinishing and so forth.     

Thermal and dynamic mechanical behavior of epoxy composites reinforced with post-consumed yerba mate

Yerba mate (YM) is widely consumed in Latin American countries, and its residues can be used as bio-resources such as reinforced in epoxy composites. The present work aims to produce epoxy resin composites and evaluate the influence of post-consumed YM as reinforcement. The concentrations of YM used were 5, 10, and 20% (wt/wt). Chemical, thermal, morphological, and dynamic mechanical behaviors were explored. The YM incorporation did not influence chemically on the epoxy structure and a pull-out phenomenon was observed as YM content increased. The YM at lower concentrations (5 and 10%) led to higher values of activation energies calculated from model-free isoconversional methods. On the other hand, the composite e/YM 20 wt% improved all dynamic-mechanical properties. YM proved to be a suitable and cheap reinforcement for epoxy resin.     

Wear and thermal behavior of basalt fiber reinforced rice husk/polyvinyl chloride composites

Plant fiber reinforced polymer composites (PFRPs) in practical application are often subjected to both complex friction and variable temperature environments. The present work explores the possibility of reinforcing rice husk/polyvinyl chloride (RH/PVC) composites with basalt fibers (BF) for developing a new wear resistant material with improved thermal stability. The results showed that the structural strength and wear resistance of the composites increased at first and then decreased with an increasing ratio of BF/RH, the highest value occurred at a BF/RH ratio of 8/42. The thermal stability of composites had a positive relationship with BF/RH ratio. The composites added with BF all possessed improved performance in comparison with unadded composites. Hence, the findings of this article proposed some new perspectives on improving the wear resistance and thermal stability of PFRPs that would broaden their practical application.     

New insight into subcritical rupture of SiC-based filaments at intermediate temperatures (400–900 °C) under air

The delayed failure of SiC fibrous reinforcement has continuously been investigated to warrant the long term performances of Ceramic Matrix Composite (CMC). Chiefly assessed on multifilament tow samples to alleviate some handling difficulties, subcritical crack growth (SCG) parameters are however ruled by structural artifacts which hinder the identification of intrinsic filament behavior. In this paper, we propose to estimate the true filament parameters for 5 fiber types from bundle behavior using a recently communicated Monte Carlo algorithm integrating flaw and stress distributions through a deterministic fracture mechanics law under Paris’ formulation. So computed tow lifetime are broadly dispersed, encompassing raw data, and show a structure-dependent scale effect, revealed by n_filament>n_tow where n is the stress exponent. The relationship between SCG coefficient and chemical composition of the substrate is discussed and highlights the major effect of doping elements (Ti or Zr), oxygen or hydrogen content.     

Preparation and antifouling performance of thin inorganic ultrafiltration membrane via assisted sol-gel method with different composition of dual additives

A novel TiO₂ thin film was prepared on the ceramic hollow fiber by the sol-gel method using poly(vinylpyrrolidone) (PVP) and polyvinyl alcohol (PVA) as additives. SEM images verified the formation of TiO₂ layer with various thickness using different composition of titania sols. The effect of the PVP and PVA contents on the TiO₂ sol properties, the separation and the antifouling performance of the ultrafiltration membranes were investigated thoroughly. When the contents of PVP and PVA were 1.0 wt% and 0.8 wt%, respectively, the resultant membrane showed a thickness of 0.55 μm with a pure water flux of 255 L m^?2 h^?1. In addition, the adherent foulant bovine serum albumin was applied to evaluate the antifouling performance. During the three fouling-recovery cycles, the flux recovery ratio and the flux decay ratio maintained about 99% and 30%. The BSA flux and rejection were still 169 L m^?2 h^?1 and 96.9% after the cycles, indicating a superior antifouling property.     

Reasonable construction of proton conducting channel via biomimetic caterpillar-like alumina fiber to improve the properties of its composite proton exchange membrane

In this paper, we prepare a novel biomimetic caterpillar-like alumina fiber with the characteristic of continuous alumina backbone and fine needle whiskers spine. Then the high-performance caterpillar-like alumina fiber composite proton exchange membrane (CAPEM) is obtained by introducing the amino modified biomimetic caterpillar-like alumina fiber into sulfonated polysulfone (SPSF) matrix, which successfully reasonable construction of the proton conducting channels in both vertical and horizontal orientation. The properties of CAPEM, including proton conductivity, methanol permeability, etc. Are systematically studied. The results show that the proton conductivity of CAPEM increases with rising the temperature, which reaches the maximum of 0.263 S/cm at 80 °C and 100% RH, respectively. The excellent proton conductivity of CAPEM is attributed to the long-range continuous proton conducting channel formed by the horizontal continuous alumina skeleton in the in-plane direction and the vertical overlapped fine needle whiskers spine in the through-plane direction. In addition, the interfacial compatibility between amino modified caterpillar-like alumina fiber and SPSF matrix is enhanced through the reasonable construction of proton conducting channels, which effectively inhibits the methanol permeation of the composite membrane with 4.18 × 10^?7 cm² s^?1 and improves the comprehensive performance of the CAPEM.     

基于蜻蜓翅脉结构的连续碳纤维增强树脂基复合材料仿生设计与增材制造

以具有轻质高强优异性能的蜻蜓翅脉结构为设计灵感，在分析翅脉网格结构抗冲击原理的基础上，设计了传统和仿生两类对比结构。采用熔融挤出3D打印机成功制备了具有不同结构的连续碳纤维增强聚乳酸复合材料试样，并对不同结构复合材料试样的拉伸性能和抗冲击性能进行了测试和对比分析。研究分析结果表明：由于拉伸力方向上的连续碳纤维含量相对较少，限制了仿生结构复合材料抗拉强度的提高，但仿生结构的平均抗拉强度为传统结构的1.18倍；当仿生结构复合材料试样受到冲击力时，其内部六边形结构的连接角度会发生变化，从而极大消耗冲击能量，同时具有六边形网格结构的连续碳纤维可以有效阻碍裂纹的扩展，因此仿生结构的平均冲击韧性可以达到传统结构的2.46倍；仿生蜻蜓翅脉结构可以显著提高增材制造复合材料的综合力学性能，且对于抗冲击性能的提高具体突出效果。连续碳纤维增强树脂基复合材料的有效可行的仿生蜻蜓翅脉结构设计和增材制造，可极大扩展其在高冲击载荷领域中的相应应用。